ORINKO Nylon Plastic Raw Material Pellets Pa6 Pa66 Gf30 Black Granules Virgin for Automobile
PA610 has good features of high strength, good wear resistance,excellent oil resistance, low water absorption, high dimension stability, excellent electric properties and so on
Feature Description：
Low water absorption
Good dimension stability
Good oil resistance, alkali resistance
High toughness, high strength
Low molding shrinkage
Excellent mouldability
PA612 has lower density，better transparence，lower water absorption，higher dimension stability，better chemical resistance，and higher impact resistance.
Feature Description：
Low water absorption
Good dimension stability
Good oil resistance, alkali resistance
High toughness, high strength
Low molding shrinkage
Excellent mouldability
PA1012 is a good substitute for PA11 and PA12, which can be used as compounds base resin.
Feature Description：
Low density
Low water absorption
Good dimension stability
Good oil resistance, alkali resistance
High toughness, high strength
Low molding shrinkage
Excellent mouldability
PA610 Item | Test Standard | Unit | Typical Value | ||
Low viscosity | Medium viscosity | High viscosity | |||
Viscosity number | GB/T 12006 ISO 307 | cm3/g | 110±20 | 145±15 | 180±20 |
Melting rang（Polarizing-microscope method） | GB/T 16582 ISO 3146 | ℃ | 222±5 | 222±5 | 222±5 |
Density | GB/T 1033 ISO 1183 | kg/m3 | 1080±2 | 1080±2 | 1080±2 |
Tensile strength | GB/T 1040 ISO 572-1/-2 | MPa | ＞55 | ＞55 | ＞55 |
Tensile modulus | GB/T 1040 ISO 572-1/-2 | MPa | ＞2000 | ＞2000 | ＞2000 |
Tensile strain at break | GB/T 1040 ISO 572-1/-2 | % | ≥100 | ≥100 | ≥100 |
Charpy impact strength（+23℃） | GB/T 1043 ISO 179/1eU | kJ/m2 | N | N | N |
Charpy impact strength（-30℃） | GB/T 1043 ISO 179/1eU | kJ/m2 | N | N | N |
Charpy notched impact strength（+23℃） | GB/T 1043 ISO 179/1eA | kJ/m2 | 4 | 4 | 4 |
Charpy notched impact strength（-30℃） | GB/T 1043 ISO 179/1eA | kJ/m2 | 5 | 5 | 5 |
Application Area
It can be widely used in the automotive industry, machinery manufacturing(oil containers, textile machinery parts), and in the electronic industry for making battrey casings, instrument rails, etc. It can also be used as bristles of toothbrushes, monofilaments and cable corerings, etc. It can be customized in injection and extrusion grade according to customers requirements.
It is mainly used as the base material for producing brake hose, fuel pipe, corrugated pipe, quick joint, the casing of ABS sensor in automobile industry and air conditioning flexible pipe etc. It is also suitable for the surface coatings of wire cable, optical fiber, metal and rope. It can be used for injection molding，extrusion， blow molding or powder coating according to customer requirements.
It is mainly used as the base material for producing brake hose, fuel pipe, corrugated pipe, quick joint, the casing of ABS sensor in automobile industry and air conditioning flexible pipe etc. It is also suitable for the
surface coatings of wire cable, optical fiber, metal and rope. It can be used for injection molding，extrusion，blow molding or powder coating according to customer requirements.