| Item | Properties | Unit | ORINKO | B**F | E*S | KI**FA |
| PA610 Inquire | Density | g/cm³ | 1.09 | |||
| Melting point 熔点 | ℃ | 213 | ||||
| Shrinkage成型收缩率 | % | 1.2 | ||||
| Tensile Strength 拉伸强度 | MPa | 60 | ||||
| Tensile Modulus拉伸模量 | GPa | 2.0 | ||||
| Elongation at break | % | 200 | ||||
| Flexural Modulus 弯曲模量 | GPa | 2.2 | ||||
| Notched impact strength 缺口冲击强度 | J/m | 56 | ||||
| Hardness 洛氏硬度 | / | 116 | ||||
| Water absorption 吸水率 | 24H-% | 0.5 | ||||
| Water absorption 吸水率 | % | 4 |
| Item | Properties | Unit | ORINKO | B**F | E*S | KI**FA |
| PA612 Inquire | Density | g/cm³ | 1.07 | |||
| Melting point 熔点 | ℃ | 210 | ||||
| Shrinkage成型收缩率 | % | 1.1 | ||||
| Tensile Strength 拉伸强度 | MPa | 62 | ||||
| Tensile Modulus拉伸模量 | GPa | 2.0 | ||||
| Elongation at break | % | 200 | ||||
| Flexural Modulus 弯曲模量 | GPa | 2.0 | ||||
| Notched impact strength 缺口冲击强度 | J/m | 54 | ||||
| Hardness 洛氏硬度 | / | 114 | ||||
| Water absorption 吸水率 | 24H-% | 0.4 | ||||
| Water absorption 吸水率 | % | 3 |
| Item | Properties | Unit | ORINKO | B**F | E*S | KI**FA |
| PA1012 Inquire | Density | g/cm³ | 1.04 | |||
| Melting point 熔点 | ℃ | 192 | ||||
| Shrinkage成型收缩率 | % | 1.0~1.5 | ||||
| Tensile Strength 拉伸强度 | MPa | 60 | ||||
| Tensile Modulus拉伸模量 | GPa | 1.5 | ||||
| Elongation at break | % | 250 | ||||
| Flexural Modulus 弯曲模量 | GPa | 1.8 | ||||
| Notched impact strength 缺口冲击强度 | J/m | 40~50 | ||||
| Hardness 洛氏硬度 | / | 100 | ||||
| Water absorption 吸水率 | 24H-% | 0.3 | ||||
| Water absorption 吸水率 | % | 2.0 |
| Item | Properties | Unit | ORINKO | B**F | E*S | KI**FA |
| PA1010 Inquire | Density | g/cm³ | 1.05 | |||
| Melting point 熔点 | ℃ | 200~210 | ||||
| Shrinkage成型收缩率 | % | 1.0~1.5 | ||||
| Tensile Strength 拉伸强度 | MPa | 55 | ||||
| Tensile Modulus拉伸模量 | GPa | 1.6 | ||||
| Elongation at break | % | 250 | ||||
| Flexural Modulus 弯曲模量 | GPa | 1.3 | ||||
| Notched impact strength 缺口冲击强度 | J/m | 40~50 | ||||
| Hardness 洛氏硬度 | / | 95 | ||||
| Water absorption 吸水率 | 24H-% | 0.39 | ||||
| Water absorption 吸水率 | % | 2.1 |
| Item | Properties | Unit | ORINKO | B**F | E*S | KI**FA |
| PA11 Inquire | Density | g/cm³ | 1.04 | |||
| Melting point 熔点 | ℃ | 187 | ||||
| Shrinkage成型收缩率 | % | 1.2 | ||||
| Tensile Strength 拉伸强度 | MPa | 55 | ||||
| Tensile Modulus拉伸模量 | GPa | 1.3 | ||||
| Elongation at break | % | 300 | ||||
| Flexural Modulus 弯曲模量 | GPa | 1.0 | ||||
| Notched impact strength 缺口冲击强度 | J/m | 40 | ||||
| Hardness 洛氏硬度 | / | 108 | ||||
| Water absorption 吸水率 | 24H-% | 0.3 | ||||
| Water absorption 吸水率 | % | 1.8 |
| Item | Properties | Unit | ORINKO | B**F | E*S | KI**FA |
| PA12 Inquire | Density | g/cm³ | 1.02 | |||
| Melting point 熔点 | ℃ | 178 | ||||
| Shrinkage成型收缩率 | % | 0.3~1.5 | ||||
| Tensile Strength 拉伸强度 | MPa | 50 | ||||
| Tensile Modulus拉伸模量 | GPa | 1.3 | ||||
| Elongation at break | % | 300 | ||||
| Flexural Modulus 弯曲模量 | GPa | 1.4 | ||||
| Notched impact strength 缺口冲击强度 | J/m | 50 | ||||
| Hardness 洛氏硬度 | / | 106 | ||||
| Water absorption 吸水率 | 24H-% | 0.25 | ||||
| Water absorption 吸水率 | % | 1.6 |
| Item | Properties | Unit | ORINKO | B**F | E*S | KI**FA |
| PA6 Inquire | Density | g/cm³ | 1.14 | |||
| Melting point 熔点 | ℃ | 220 | ||||
| Shrinkage成型收缩率 | % | 0.6~1.6 | ||||
| Tensile Strength 拉伸强度 | MPa | 74 | ||||
| Tensile Modulus拉伸模量 | GPa | 2.5 | ||||
| Elongation at break | % | 200 | ||||
| Flexural Modulus 弯曲模量 | GPa | 2.6 | ||||
| Notched impact strength 缺口冲击强度 | J/m | 56 | ||||
| Hardness 洛氏硬度 | / | 114 | ||||
| Water absorption 吸水率 | 24H-% | 1.8 | ||||
| Water absorption 吸水率 | % | 10.7 |
| Item | Properties | Unit | ORINKO | B**F | E*S | KI**FA |
| PA66 Inquire | Density | g/cm³ | 1.14 | |||
| Melting point 熔点 | ℃ | 260 | ||||
| Shrinkage成型收缩率 | % | 0.8~1.5 | ||||
| Tensile Strength 拉伸强度 | MPa | 80 | ||||
| Tensile Modulus拉伸模量 | GPa | 2.9 | ||||
| Elongation at break | % | 60 | ||||
| Flexural Modulus 弯曲模量 | GPa | 3.0 | ||||
| Notched impact strength 缺口冲击强度 | J/m | 40 | ||||
| Hardness 洛氏硬度 | / | 118 | ||||
| Water absorption 吸水率 | 24H-% | 1.3 | ||||
| Water absorption 吸水率 | % | 8.5 |