Typical Display | PLA Resin | Modified Biodegradable Material | ||||||||
HT102 | HT202 | HT503 | M1000 | M2000 | M5000-5C | H8000-1A | H8000-2D | H8000-3D | ||
Application process | Blow Molding | ● | ● | ● | ● | ● | ||||
Extrusion/Thermoforming | ● | ● | ● | |||||||
Injection Molding | ● | ● | ||||||||
Density | g/cm3 | 1.24±0.05 | 1.24±0.05 | 1.24±0.05 | 1.20-1.30 | 1.20-1.30 | 1.25-1.45 | 1.30-1.34 | 1.32-1.35 | |
Melt Flow Rate | （g/10min) 190℃ /2.16kg | 2-9 | 10-25 | 2-6 | 2-4 | 2-4 | 2-4 | 4-6 | 4-7 | |
Melting temperature | ℃ | 160-174 | 160-174 | <160 | / | / | / | / | / | |
Glass transition temperatur | ℃ | 58-62 | 58-62 | 58-62 | / | / | / | / | / | |
Tensile strength | MPa | ≥50 | ≥45 | ≥50 | ≥12 | ≥14 | ≥12 | ＞40 | ＞50 | |
Elongation at break | % | ＜5 | ＜5 | ＜5 | ≥350 | ≥300 | ≥250 | ＞5 | ＞5 | |
The key feature of the flexible biodegradable materials film grades is the certified compostability. Independent agencies confirm that biodegradable materials passes the strict testing criteria of the standard and are ultimately converted into water, CO2 and biomass in industrial composting facilities, just as organic waste. The main applications are low gauge bags, magazine envelopes, mulch films and food packaging.
Type | Density （g/cm3） | MFR（g/10min） | Moisture (%) | Ash (%) | Tensile Strength(MPa) | Elongation at break (%) |
M2000 | 1.20-1.25 | 2-4 | <0.09 | <5 | ＞12 | ＞450 |
Typical Display | PLA Resin | Modified Biodegradable Material | ||||||||
HT102 | HT202 | HT503 | M1000 | M2000 | M5000-5C | H8000-1A | H8000-2D | H8000-3D | ||
Application process | Blow Molding | ● | ● | ● | ● | ● | ||||
Extrusion/Thermoforming | ● | ● | ● | |||||||
Injection Molding | ● | ● | ||||||||
Density | g/cm3 | 1.24±0.05 | 1.24±0.05 | 1.24±0.05 | 1.20-1.30 | 1.20-1.30 | 1.25-1.45 | 1.30-1.34 | 1.32-1.35 | |
Melt Flow Rate | （g/10min) 190℃ /2.16kg | 2-9 | 10-25 | 2-6 | 2-4 | 2-4 | 2-4 | 4-6 | 4-7 | |
Melting temperature | ℃ | 160-174 | 160-174 | <160 | / | / | / | / | / | |
Glass transition temperatur | ℃ | 58-62 | 58-62 | 58-62 | / | / | / | / | / | |
Tensile strength | MPa | ≥50 | ≥45 | ≥50 | ≥12 | ≥14 | ≥12 | ＞40 | ＞50 | |
Elongation at break | % | ＜5 | ＜5 | ＜5 | ≥350 | ≥300 | ≥250 | ＞5 | ＞5 | |
The key feature of the flexible biodegradable materials film grades is the certified compostability. Independent agencies confirm that biodegradable materials passes the strict testing criteria of the standard and are ultimately converted into water, CO2 and biomass in industrial composting facilities, just as organic waste. The main applications are low gauge bags, magazine envelopes, mulch films and food packaging.
Type | Density （g/cm3） | MFR（g/10min） | Moisture (%) | Ash (%) | Tensile Strength(MPa) | Elongation at break (%) |
M2000 | 1.20-1.25 | 2-4 | <0.09 | <5 | ＞12 | ＞450 |